Chemical-pressure tailoring of low-field, room temperature magnetoresistance in (ca, sr, ba) fe.0.5mo0.5o3

ABSTRACT

The room temperature, low field intergrain magnetoresistance (IMR) of the double perovsktite SrFe 0.5 MO 0.5 O 3  is found to be highly tunable by doping either Ca or Ba into the Sr site. The dopant exerts a chemical pressure, changing the Curie temperature and the magnetic softness. The IMR at optimal doping (Sr 0.2 Ba 0.8 Fe 0.5 Mo 0.5 O 3 ) is approximately 3.5% in 100 Oe, and increases further in high fields. The unprecedented strength of the IMR in this highly spin polarized system provides new grounds for employing novel magnetic materials for new magnetic sensing applications and spin electronics.

FIELD OF THE INVENTION

[0001] This invention relates to magnetic material systems, and more particularly to double perovskite material systems having large magnitude room temperature IRs.

BACKGROUND OF THE INVENTION

[0002] The impending ability to manipulate electron spins using emerging technology and the need for ever-increasing magnetic storage density have driven researchers to search for novel ferromagnetic materials other than Fe, Co, Ni and their alloys. Remarkable phenomena, such as colossal magnetoresistance (CMR) and quantum-interference magnetoresistance have been discovered in these new materials. Unfortunately, most of these effects are only realized at low temperatures and in high magnetic fields, making potential applications impractical. For example, perovskite (or pyrochlore) manganites and related compounds exhibit CMR in the vicinity of the metal-insulator transition temperature. However, this only occurs below room temperature and under applied fields of several tesla.

[0003] Other novel materials, such as silver chalcogenides (Ag_(2+δ)Se, Ag_(2+δ)Te), CrO₂, doped iron silicide (Fe_(1-x)Co_(x)Si, Fe_(1-x)Mn_(x)Si), and inhomogeneous semiconductors such as Hg_(1-x)Cd_(x)Te, also exhibit significant magnetoresistance (MR) only at low temperatures and/or in high fields. One interesting approach to reduce the field strength required to observe a large MR is to utilize tunneling MR (TMR) in either multilayer structures or granular (polycrystalline) materials.

[0004] Intergrain magnetoresistance (SIR) originates from the change of grain-to-grain electron tunneling in polycrystalline materials under applied magnetic fields. This effect becomes significant in materials where the spins of the itinerant electrons are highly polarized. In the so-called half metals, the carrier spins are completely polarized. These systems exhibit metallic transport behavior for one spin orientation and insulating behavior for the other. However, significant IMR only occurs below the Curie temperature (Tc), and thus room temperature IMM does not exist in Tl₂Mn₂O₇ (Tc≈120° K.) and is nearly absent in perovskite manganites and CrO₂.

[0005] Recent interest has been focused on the double perovskite material systems such as SrFe_(0.5)Mo_(0.5)O₃, due to the large magnitude of the room temperature IMR. SrFe_(0.5)Mo_(0.5)O₃ has an IM of about 5% at room temperature in magnetic fields of about 10 kOe. The large fields required to achieve this level of IMR probably originate from the high saturation field in this material, and seriously limit the technological applications. For example, the field strength required for magnetic heads is in the range of a few hundred Oe. It is common practice to control magnetic softness by adjusting the magneto-elastic coupling through alloying. For example, the alloying of Ni with Fe significantly lowers the coercive and saturation fields. Furthermore, it has been well established that the substitution of different-size ions into the A-site of AMnO₃ exerts a “chemical pressure” on the system. This chemical pressure causes pronounced changes in physical properties of the system such as T_(C) and CMR.

[0006] Accordingly, it would be desirable to reduce the magnetic fields required for achieving the large magnitude room temperature IMRs in double perovskite material systems.

SUMMARY OF THE INVENTION

[0007] In accordance with a first aspect of the present invention, a magnetoresistive material system and a magnetic field sensing device made from same comprises Sr_(1-x)Ba_(x) Fe_(0.5)Mo_(0.5)O₃, wherein x is about 0.1 to about 1.0. When x is about 0.8, the first embodiment of the material system exhibits a magnetoresistance change of about 3.5 percent in a magnetic field of about 100 Oe at room temperature, and a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.

[0008] In accordance with a second aspect of the present invention , a magnetoresistive material system and a magnetic field sensing device made from same comprises Sr_(1-x)Ca_(x)Fe_(0.5)Mo_(0.5)O₃, wherein x is about 0.01 to about 0.1. When x is about 0.05, the second embodiment of the material system exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009]FIG. 1A is a graph showing normalized resistivity versus magnetic field at room temperature in Sr_(1-y)Ba_(y)Fe_(0.5)Mo_(0.5)O₃ and other materials;

[0010]FIG. 1B is a graph showing normalized resistivity versus magnetic field up to 10 kOe in Sr_(0.2)Ba_(0.8)Fe_(0.5)Mo_(0.5)O₃ and Sr_(0.95)Ca_(0.05)Fe_(0.5)Mo_(0.5)O₃;

[0011]FIG. 2 is a graph showing change of resistivity as a function of Ca (x) or Ba (y) concentration in three magnetic fields: 0.25 kOe (square), 2 kOe (circle) and 10 kOe (triangle);

[0012]FIG. 3 is a magnetic phase diagram plotting T_(C) as a function of Ca (x) or Ba (y) concentration;

[0013]FIG. 4A is a graph showing normalized magnetization as a function of magnetic field for BaFe_(0.5)Mo_(0.5)O₃, SrFe_(0.5)Mo_(0.5)O₃, and CaFe_(0.5)Mo_(0.5)O₃; with the magnetic hysteresis loop of Sr_(0.2)Ba_(0.8)Fe_(0.5)Mo_(0.5)O₃ shown in inset;

[0014]FIG. 4B is a graph showing x-ray diffraction intensity versus 2θ for BaFe_(0.5)Mo_(0.5)O₃, SrFe_(0.5)Mo_(0.05)O₃, CaFe_(0.5)Mo_(0.5)O₃, and Sr_(1-x)Ca_(x)Fe_(0.5)Mo_(0.5)O₃; and

[0015]FIG. 5 is a schematic representation of an exemplary device made according to the principles of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0016] The present invention is directed to magnetoresistive, Fe—Mo double perovskite material systems, specifically (Ca, Sr, Ba)Fe_(0.5)Mo_(0.5)O₃ material systems having chemical pressure tuned T_(C)s and the room temperature IMRs. In the discussion which follows, the formula Fe_(0.5)Mo_(0.5)O₃ will be denoted as FMO.

[0017] A first embodiment of the material system of the present invention comprises Sr_(1-x)Ba_(x)FMO, where x is about 0.1 to about 1.0. The preferred composition of this system, Sr_(0.2)Ba_(0.8)FMO, exhibits a significantly enhanced low-field (100 Oe range) IMR, which is associated with soft magnetic behaviors. In particular, polycrystalline Sr_(0.2)Ba_(0.8)FMO exhibits an unprecedented IMR value of approximately 3.5% in 100 Oe at room temperature, which increases to 8% in 1 kOe. This large low-field IMR accompanies a negligible field hysteresis, which is consistent with the small coercive field (less than 10 Oe) of this material.

[0018] A second embodiment of the material system of the present invention comprises Sr_(1-x)Ca_(x)Fe_(0.5)Mo_(0.5)O₃, where x is about 0.01 to about 0.1. IMR in the field range of a few kOe is optimized at the preferred composition of Sr_(0.95)Ca_(0.05)FMO, which is associated with an enhanced ferrimagnetic transition temperature.

[0019] The double perovskite material systems of the present invention are intended for use in magnetic and electronic technologies. More specifically, as shown in FIG. 5, the double perovskite material systems of the present invention may be used for constructing a magnetic field sensor 10 utilized in a magnetic and/or electronic device 20 including, but not limited to, a magnetic read head for a hard disk, a speed sensor, and a gauss meter. Further the double perovskite material systems of the present invention may also be useful in other devices and applications which utilize magnetic field sensing elements.

Exemplary Sample Preparations and Experimental Test Results

[0020] A series of polycrystalline Sr_(1-x)Ca_(x)FMO and Sr_(1-y)Ba_(y)FMO samples were prepared by standard solid-state reaction under a 2% H₂/N₂ atmosphere. The samples were analyzed using X-ray diffraction by means of Rigaku D-max . The X-ray diffraction data demonstrated that the samples were single phase. Superlattice peaks indicating Fe—Mo ordering were also observed. The MR of the samples in fields up to 10 kOe was measured at room temperature using a conventional four-probe technique in the longitudinal geometry. Magnetization was measured by a Quantum Design SQUID magnetometer, and T_(C) was precisely determined from AC susceptibility measurements (about 1 Oe) taken above 300 K.

[0021] Optimal low-field IMR was observed in Sr_(0.2)Ba_(0.8)FMO. FIG. 1A is graph showing normalized resistivity versus magnetic field at room temperature in Sr_(1-y)Ba_(y)Fe_(0.5)Mo_(0.5)O₃ and the other materials, where y equals 0.8 (depicted with circles) and y equals 0.5 (depicted with squares). As shown, the low-field IMR in the material systems of the present invention are much larger than in prior art material systems. The CMR manganite (La_(5/8)Sr_(3/8)MnO₃) and SrFMO show less than 1% negative MR in 300 Oe, and silver telluride exhibits about 0.5% positive MR in 300 Oe. The Sr_(0.2)Ba_(0.8)FMO sample of the present invention shows 2% MR in 50 Oe, 3.5% MR in 100 Oe, and 5.7% MR in 300 Oe. The Sr_(0.5)Ba_(0.5)FMO sample shows slightly reduced MR. No measurable field hysteresis is associated with the MR of the Sr_(1-y)Ba_(y)Fe_(0.5)Mo_(0.5)O₃ materials of the present invention. The magnetization measurement shows the coercive field of this material system to be less than 10 Oe (FIG. 4A inset). Note that to minimize the demagnetization factor, needle-shaped samples were measured with the field along the longitudinal direction of the samples. However, voids in the polycrystalline samples can contribute to the demagnetization factor. Therefore, low-field MR should be larger in polycrystalline thin films made in accordance with the present invention.

[0022]FIG. 1B is a graph showing the room temperature MR of various compositions of (Ca,Sr,Ba)FMO measured in fields up to 10 kOe (depicted with solid lines). For comparison, MR values reported for prior art SrFMO and BaFMO were included (depicted with dashed lines). The MR of CaFMO was small (˜1% in 10 kOe) compared with that of SrFMO and BaFMO (˜5-6% in 10 k0e). The values of the 10 kOe MR are comparable to those in the prior art. However, the MR response of the Ba sample of the present invention to small magnetic fields (<1 kOe) was more dramatic than the NMR response of the prior art samples. Sr_(0.95)Ca_(0.05)FMO (depicted with triangles) and Sr_(0.2)Ba_(0.8)FMO (depicted with circles) appear to be optimum compositions with respect to MR. In the Sr_(1-x)Ca_(x)FMO series, Sr_(0.95)Ca_(0.05)FMO is the optimal composition, showing approximately 11% NMR in 10 kOe. In the Sr_(1-y)Ba_(y)FMO series, NMR (about 11% NMR in 10 kOe) is optimized in the composition of Sr_(0.2)Ba_(0.8)FMO.

[0023] IMR varies non-monotonically with the variation of chemical pressure, which increases with decreasing ionic size. FIG. 2 shows the change of MR as a function of composition (i.e. average ionic size) in three different fields: 0.25 kOe (depicted with squares), 2 kOe (depicted with circles), and 10 kOe (depicted with triangles). Prior art values for SrFMO and BaFMO are also shown for comparison. Solid symbols represent the results from the present invention, and open symbols represent results from the prior art, respectively. Lines are drawn as guides for the eye. The MR of SrFMO is consistent with the prior art for all fields studied. However, in the case of BaFMO, the observed NMR in 0.25 kOe is much larger than the prior art value even though the MR in 10 kOe is similar to that in the prior art. The, Sr_(0.2)Ba_(0.8)FMO sample of the present invention exhibited the largest MR (5%) at 0.25 kOe. A common feature of the Sr_(1-y)Ba_(y)FMO series is this enhancement of the low-field MR, which can clearly be seen in the 0.25 kOe data. The NMR (especially, at 10 kOe) of the Sr_(1-x)Ca_(x)FMO series is sharply maximized at x=0.05. Even though this feature persists down to low fields, the low-field MR of Sr_(0.95)Ca_(0.05)FMO is relatively small, compared to that of the Sr_(1-y)Ba_(y)FMO series. This remarkable enhancement of high-field MR disappears rapidly with further doping of Ca (FIG. 2, inset). Hence, the MR behavior shows two important features: 1) drastic enhancement of low-field MR in the Ba doping region with the optimization of low-field MR at Sr_(0.2)Ba_(0.8)FMO, and 2) enhanced MR at ˜5% Ca doping (Sr_(0.95)Ca_(0.05)FMO) for high fields with an abrupt drop of the MR at ˜10% Ca doping.

[0024] In order to understand this non-monotonic MR behavior, reference should now be made to FIG. 3 which shows a magnetic phase diagram based on alternating current (AC) susceptibility, χ, as a function of temperature comparing the material system of the present invention with prior art values. Solid symbols represent the samples of the present invention and open symbols (depicted with circles and triangles) represent the prior art. For the end members, there exists a slight discrepancy between T_(C) in the samples of the present invention and in the prior art, which might reflect a slight variation of stoichiometry. The T_(C) for the Sr_(1-y)Ba_(y)FMO samples of the present invention tends to decrease monotonically from 404 K. (y=0) to 318 degrees K. (y=1) with increasing Ba concentration. For the Sr_(1-x)Ca_(x)FMO samples of the present invention, there exists a slow increase of T_(C) as x increases, which is followed by a sharp drop of T_(C) when x reaches 0.07-0.1. For x larger than 0.1 T_(C) decreases monotonically to that of the Ca end member.

[0025]FIG. 4A shows the normalized magnetization of three different samples at room temperature, and the inset of FIG. 4A depicts the hysteresis loop for Sr_(0.2)Ba_(0.8)FMO. The rapid rise of the low-field magnetization of the BaFMO sample (depicted with a solid line), compared with that of the CaFMO sample (depicted with a short dashed line) and the SrFMO (depicted with a dashed line) sample, indicates that the BaFMO is magnetically soft. The magnetization of the BaFMO in 0.25 kOe is more than 60% of the 15 kOe magnetization value. It was generally found that Ba-doped samples are magnetically softer than Ca-doped samples. For example, the magnetization of the Ca-doped samples in 0.25 kOe is about 45% of the 15 kOe magnetization value. This magnetic softness is also evident in the AC susceptibility data. The AC susceptibility of the Ba-doped samples is about three times larger than that of the Ca-doped samples.

[0026]FIG. 4B show x-ray results that reveal an intriguing structural evolution with chemical pressure. First of all, the (quasi-) cubic perovskite x-ray pattern with Kα1 and Kα2 splitting is consistent with those of BaFMO and SrFMO. However, the CaFMO pattern shows clear monoclinic splitting, indicating significant structural distortions in the Ca compound. No drastic change of the x-ray pattern was observed in Sr_(1-x)Ca_(x)FMO with Ca doping up to x=0.05, but peak broadening was evident for Ca concentrations beyond x≈0.07. This x-ray peak broadening indicates that the average structure is close to that of a (quasi-) cubic perovskite, but there exist local incoherent structural distortions in the Ca-doped materials with x=0.1-0.5.

[0027] The evolution of T_(C) in (Ca,Sr,Ba)FMO with chemical pressure can be understood in terms of crystallographic change and the consequent change in the electron hopping. In the ordered Fe—Mo double perovskites, AFMO, the B site ions order in the NaCl structure due to their charge and size differences, and thus each Fe—O octahedron is surrounded by six Mo—O octahedra, and vice versa. A simple ionic consideration shows that the valence of Fe is 3+(3d⁵, S=5/2) and that of Mo is 5+(4d¹, S=1/2). Mo t_(2g) electrons are supposed to be itinerant, and thus two hopping mechanisms need to be considered: the double-exchange-like hopping in Mo—O—Fe and the direct Mo—Mo hopping. Chemical pressure can influence the electron hopping (i.e., electron band width (W)) through the change of structural parameters such as the bond lengths and bond angles of Mo—O—Fe and Mo—Mo. X-ray results indicate that by changing the composition from BaFMO to Sr_(0.95)Ca_(0.05)FMO (i.e., increasing chemical pressure), the structure remains as (quasi-) cubic, and Mo—O—Fe, and Mo—Mo bond angles do not change much (they remain as about 180°). However, Mo—O—Fe and Mo—Mo bond lengths decrease, and thus W increases with increasing chemical pressure, which is consistent with the enhancement of T_(C). On the other hand, upon further increasing chemical pressure from Sr_(0.95)Ca_(0.05)FMO to CaFMO, the structure changes from (quasi-) cubic to monoclinic, which ought to influence not only bond distances but also bond angles significantly. Thus, electron hopping can be reduced in monoclinic CaFMO, which is in accordance with the decreased T_(C) in the CaFMO. Consistently, the abrupt decrease of T_(C) near Sr_(0.9)Ca_(0.1)FMO occurs at the composition where x-ray peak broadening occurs, indicating local structural distortions. It is emphasize that, compared to e_(g) orbitals in manganites, the relevant orbital hopping path for Fe—O—Mo is t_(2g)-p_(π)-t_(2g) so that the chemical pressure effect on T_(C) is expected to be much smaller than that of the manganites due to their bonding geometry. However, the direct hopping between diagonal Mo ions is presumably sensitive to structural parameters, especially the bond angle.

[0028] The intriguing evolution of MR behavior with chemical pressure (FIG. 2) can be qualitatively understood from the concomitant change of T_(C) (FIG. 3) and magnetic softness (FIG. 4A). In general, the system of the present invention becomes magnetically softer with increasing Ba concentration, and BaFMO shows a rapid rise of the magnetization with increasing magnetic field (FIG. 4A). Even though x-ray results indicate that the structure is always (quasi-) cubic for the Sr—Ba system, the detailed crystallographic study has shown that there exists a slight tetragonal distortion in the Sr system, and the Ba system is simple cubic. Thus, when the structure approaches simple cubic with Ba doping, the magneto-elastic coupling should be reduced, and consequently the system becomes magnetically soft. Evidently, the low-field IMR can be enhanced when the system becomes magnetically soft. However, T_(C) decreases with increasing Ba concentration. These two competing effects optimize low-field, room temperature IMR at the composition of Sr_(0.2)Ba_(0.8)FMO. If in fields of a few kOe is more sensitive to T_(C) than magnetic softness. Thus, Sr_(0.95)Ca_(0.05)FMO, optimized with respect to T_(C), results in maximal IMR infields of a few kOe.

[0029] While the foregoing invention has been described with reference to the above embodiments, various modifications and changes can be made without departing from the spirit of the invention. Accordingly, such modifications and changes are considered to be within the scope of the appended claims. 

What is claimed is:
 1. A magnetoresistive material system comprising Sr_(1-x)Ba_(x)Fe_(0.5)Mo_(0.5)O₃, wherein x is about 0.1 to about 1.0.
 2. The material system according to claim 1, wherein x is about 0.8.
 3. The material system according to claim 2, wherein the material system exhibits a magnetoresistance change of about 3.5 percent in a magnetic field of about 100 Oe at room temperature.
 4. The material system according to claim 2, wherein the material system exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.
 5. A magnetoresistive material system comprising Sr_(1-x)Ca_(x)Fe_(0.5)Mo_(0.5)O₃, wherein x is about 0.01 to about 0.1.
 6. The material system according to claim 5, wherein x is about 0.05.
 7. The material system according to claim 5, wherein the material system exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.
 8. A magnetic field sensing device comprising a Sr_(1-x)Ba_(x)Fe_(0.5)Mo_(0.5)O₃ material system, wherein x is about 0.1 to about 1.0.
 9. The magnetic field sensing device according to claim 8, wherein x is about 0.8.
 10. The magnetic field sensing device according to claim 9, wherein the device exhibits a magnetoresistance change of about 3.5 percent in a magnetic field of about 100 Oe at room temperature.
 11. The magnetic field sensing device according to claim 9, wherein the device exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.
 12. A magnetic field sensing device comprising a Sr_(1-x)Ca_(x)Fe_(0.5)Mo0.5O₃ material system, wherein x is about 0.01 to about 0.1.
 13. The magnetic field sensing device according to claim 12, wherein x is about 0.05.
 14. The magnetic field sensing device according to claim 13, wherein the device exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.
 15. A method of tuning room temperature, low field intergrain magnetoresistance of an SrFe_(0.5)Mo_(0.5)O₃ material system, the method comprising the step of doping a dopant into the Sr site of the SrFe_(0.5)Mo_(0.5)O₃ material system.
 16. The method according to claim 15, wherein the dopant consists essentially of Ba and doping is performed to form an Sr_(1-x)Ba_(x)Fe_(0.5)Mo_(0.5)O₃ material system, wherein x is about 0.1 to about 1.0.
 17. The method according to claim 16, wherein x is about 0.8.
 18. The method according to claim 17, wherein the material system exhibits a magnetoresistance change of about 3.5 percent in a magnetic field of about 100 Oe at room temperature.
 19. The method according to claim 17, wherein the material system exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature.
 20. The method according to claim 15, wherein the dopant consists essentially of Ca and doping is performed to form an Sr_(1-x)Ca_(x)Fe_(0.5)Mo0.5O₃ material system, wherein x is about 0.01 to about 0.1.
 21. The method according to claim 20, wherein x is about 0.05.
 22. The method according to claim 21, wherein the material system exhibits a magnetoresistance change of about 11 percent in a magnetic field of about 10 kOe at room temperature. 